| About |
|---|
| Overview PULSE™ 2000EZ is a high-heat PC/ABS resin delivering optimized performance for automotive interior component applications. Benefits Easy flow, reduced scrap, and faster cycle times, while enabling thin wall part design for mass reduction. High-impact strength even at low temperature High Heat resistance for demanding automotive interior components Consistent natural white color produces high quality part appearance when used with color concentrates (self coloring) or Trinseo Color Masterbatch Technology Low odor & VOC to meet all global Automotive OEM specifications Applications: Mid (floor)consoles Instrument Panel components Door panel trim Pillars Storage / load floors / glove box&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Latin America,North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.13 | g/cm³ | ASTM D792，ISO 1183-A |
| — | 1.13 | g/cm³ | ISO 1183-1 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.7 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 18 | g/10min | ASTM D1238，ISO 1133 |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570，ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 2330 | MPa | ISO 527-2 |
| — | 2350 | MPa | ISO 527-2 3 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 57.0 | MPa | ISO 527-2/50 |
| yield | 54.0 | MPa | ISO 527-2 5 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 47.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.5 | % | ISO 527-2/50 |
| yield | 4.4 | % | ISO 527-2 7 |
| fracture | 160 | % | ASTM D638 |
| fracture | 90 | % | ISO 527-2/50 |
| Strain, fracture | > 50 | % | ISO 527-2 8 |
| Bending modulus | |||
| — | 2450 | MPa | ASTM D790 |
| — | 2400 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 12 | ||
| -30℃ | 14.0 | kJ/m² | 13 |
| 23℃ | 40.0 | kJ/m² | 14 |
| Charpy impact strength | ISO 179/1eU 15 | ||
| -30℃ | 无断裂 | 16 | |
| 23℃ | 无断裂 | 17 | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 590 | J/m | ASTM D256 |
| 23℃ | 750 | J/m | ASTM D256 |
| -30℃ | 47 | kJ/m² | ISO 180-A |
| 23℃ | 63 | kJ/m² | ISO 180-A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| 23℃，Total Energy | 62.0 | J | |
| 23℃，Peak Energy | 55.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | ISO 75-2/B |
| 0.45 MPa | 126 | ℃ | ISO 75-2 19 |
| 1.8 MPa, unannealed | 109 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 106 | ℃ | ISO 75-2/A |
| 1.8 MPa | 105 | ℃ | ISO 75-2 20 |
| Vicat Softening Temp | |||
| — | 142 | ℃ | ISO 306/A120 |
| B50 | 129 | ℃ | ISO 306 |
| B50 | 124 | ℃ | ISO 306 21 |
| Linear coefficient of thermal expansion | |||
| MD | 6.9E-5 | 1/℃ | ISO 11359-2 22 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 4 | hr | |
| Melt Temperature | 255-290 | ℃ | |
| Mold Temperature | 60-80 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. Mold Temperature: 140°F, Melt Temperature: 500°F, Injection Pressure: 2.61E+4 psi |
| 4. 0.039 in/min |
| 5. 0.079 in/min |
| 6. Type 1, Edgewise, Notch A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |