| PULSE™ 6000 BG is a PC/ABS resin offering an interesting combination of heat ageing characteristics, low temperature impact performance and high melt strength. Its low MFR enables manufacturing of complex blow molding parts. Typical applications for this product are Blow Molded Spoilers, knee bolsters and Seat Backs.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good melt strength,low-temperature impact resistance |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 6.0 | g/10min | ISO 1133 |
| 260℃，5.0kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.53 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2160 | MPa | ASTM D638 |
| Tensile modulus | 2280 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 54.5 | MPa | ASTM D638 |
| fracture | 53.0 | MPa | ISO 527-2 |
| yield | 54.0 | MPa | ISO 527-2 |
| yield | 51.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 80 | % | ASTM D638 |
| fracture | > 80 | % | ISO 527-2 |
| yield | 5.0 | % | ISO 527-2 |
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 68.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 50 | kJ/m² | ISO 179 |
| 23℃ | 61 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 640 | J/m | ASTM D256 |
| 23℃ | 750 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/4A | ||
| -40℃ | 61 | kJ/m² | ISO 180-4A |
| 23℃ | 69 | kJ/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 111 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 144 | ℃ | ISO 306/A120 |
| B50 | 130 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 7.4E-5 | 1/℃ | ASTM D696 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 3 points |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |