| About |
|---|
| An inherently matt medium heat, medium impact PC/ABS resin, PULSE™ 920 MG is designed for interior automotive applications where a matt aesthetic is required. Proprietary low gloss technology allows this unique combination of maximum low gloss aesthetics and physical properties.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Heat Resistance, Good,Low Gloss,HB |
| Availabilitys | Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183/B |
| Density | 1.13 | g/cm³ | ISO 1183-2 |
| Apparent density | 0.65 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 17 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 260℃，5 kg | 15.0 | cm³/10min | ISO 1133 |
| Spiral flow length | 51.0 | cm | |
| Shrinkage rate | 0.35 to 0.45 | % | ISO 294-4 |
| Water absorption rate | |||
| saturated | 0.030 | % | ISO 62-2 |
| balance | 0.28 | % | ISO 62-2 |
| VOC Content | 9.00 | µg/g | VDA 277 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2250 | MPa | ISO 527-1-2 |
| Tensile modulus | 2050 | MPa | ISO 527-2 2 |
| tensile strength | |||
| yield | 48.0 | MPa | ISO 527-2 2 |
| yield | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 100 | % | ISO 527-2/50 |
| yield | 4.6 | % | ISO 527-2 2 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | 2100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 23℃ | 45.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 30.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 7.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 22 | kJ/m² | ISO 179/1eA |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 105 | ℃ | ISO 75-2/A |
| 1.8 MPa | 102 | ℃ | ISO 75-2 2 |
| 0.45 MPa | 126 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 122 | ℃ | ISO 306 |
| B50 | 128 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 7.3E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. Melt Temperature: 500°F, Injection Pressure: 2.61E+4 psi |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |