| PULSE™ EXT 100 engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at room and low temperatures. PULSE EXT 100 engineering resin has been used in automotive plated and painted exterior trim applications. Applications: Front Grilles Wheel Covers and Center Caps Decorative Trim Name Plates and Badges&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High Heat Resistance,low-temperature impact resistance |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2100 | MPa | ISO 527-2 2 |
| tensile strength | |||
| yield | 54.0 | MPa | ISO 527-2 2 |
| yield | 51.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 80 | % | ASTM D638 |
| yield | 4.8 | % | ISO 527-2 2 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | 2240 | MPa | ASTM D790 |
| bending strength | |||
| yield | 82.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 61.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 24.0 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 480 | J/m | ASTM D256 |
| 23℃，3.2mm | 640 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -29℃，3.20 mm，Total Energy | 59.9 | J | ASTM D3763 |
| 23℃，3.20 mm，Total Energy | 54.2 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 107 | ℃ | ASTM D648 |
| 1.8 MPa | 111 | ℃ | ISO 75-2 2 |
| 0.45 MPa, unannealed, 3.2 mm | 124 | ℃ | ASTM D648 |
| 0.45 MPa | 134 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 133 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 7.2E-5 | 1/℃ | ASTM D696 |
| MD | 7.2E-5 | 1/℃ | ISO 11359-2 2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D792 |
| Density | 1.14 | g/cm³ | ISO 1183-2 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 1.3 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D955 |
| Melt density | 1.02 | g/cm³ | |
| Melt Specific Heat | 1980 | J/kg/℃ | ASTM C351 |
| Melt thermal conductivity | 0.26 | W/m/K | ASTM C177 |
| No Flow Temperature | 160 | ℃ | |
| Ejection temperature | 138 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. Type I, 2.0 in/min |
| 4. 10 mil Notch Depth |
| 5. 11.1 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |