| About |
|---|
| PULSE™ GX50 NA is a very low gloss appearance engineering resin which has exceptional impact strength even at low temperatures and has sufficient heat resistance for the majority of automotive interior components. This resin provides excellent flow, has low odor & VOC values and is self colorable. This material has superior low gloss performance over typical PC/ABS. Applications: PULSE GX50 NAB is used in a wide range of applications where low temperature toughness and tailor made heat resistance is required.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,High liquidity,High Heat Resistance,Low odor,low-temperature impact resistance,Low Gloss |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183/B |
| Apparent density | 0.63 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 12 | g/10min | ISO 1133 |
| Spiral flow length | 58.0 | cm | |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| VOC Content | 10.0 | µg/g | VDA 277 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 43.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 80 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 50 | kJ/m² | ISO 179/1eA |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 93.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 109 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 7.5E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 255 to 280 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 500°F, Injection Pressure: 2,61E+4 psi |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |