| About |
|---|
| Overview PULSE™ GX90 is a super low temperature ductile, high-heat, low gloss PC/ABS resin delivering optimized performance for automotive interior component applications. Benefits Outstanding high-impact strength even at low temperature High Heat resistance for demanding automotive interior components Consistent natural white color produces high quality part appearance when used with color concentrates (self coloring) or Trinseo Color Masterbatch Technology Low odor & VOC to meet all global Automotive OEM specifications Applications Mid (floor)consoles Instrument Panel components Door panel trim Pillars Storage / load floors / glove box&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good liquidity,High Heat Resistance,Low odor,low-temperature impact resistance |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183/B |
| Apparent density | 0.65 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 17 | g/10min | ISO 1133 |
| Spiral flow length | 48.0 | cm | |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| VOC Content | 9.00 | VDA 277 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 4 mm, injection molding | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 110 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 55 | kJ/m² | ISO 179/1eA |
| 23℃ | 55 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 106 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 123 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 500°F, Injection Pressure: 2,61E+4 psi |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |