| Homo PLA: improved modulus PLA blends based on monomers from Purac offer: Heat resistance up to 120°C (HDT B) Good processing economics Impact resistance comparable to ABS Biobased content Multiple end-of-life options Existing commercial availability Blend B: to achieve a higher modulus, and an even higher temperature resistance, talc was added to blend A (see blend B in the table below).&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,Nucleation,High Heat Resistance,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | |
| tensile strength | 42.0 | MPa | |
| Tensile strain | |||
| fracture | 17 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 120 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Flatwise |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |