| About |
|---|
| Pyramid™ KD2530-NT is a Polyetheretherketone (PEEK) product filled with 20% ptfe fiber. It is available in North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Lubricating,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 43 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 171 | ℃ | ASTM D648 |
| Glass transition temperature | 143 | ℃ | DSC |
| Melting temperature | 343 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 | ASTM D2240 | |
| Tensile modulus | 3170 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 79.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 3450 | MPa | ASTM D790 |
| bending strength | |||
| yield | 138 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.10 | ASTM D1894 | |
| With oneself – static | 0.10 | ASTM D1894 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |