| QAMAR FC18N is a Linear Low Density Polyethylene material. It is available in Africa & Middle East, Asia Pacific, Europe, or North America for blown film. Typical application of QAMAR FC18N: Film&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D4883 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1872-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD，30 µm | 190 | MPa | ISO 527-3 |
| TD，30 µm | 220 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| yield | 9.00 | MPa | ISO 1872-2 |
| MD, fracture, 30 µ m | 55.0 | MPa | ISO 527-3 |
| TD, fracture, 30 µ m | 40.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| fracture | > 430 | % | ISO 1872-2 |
| MD, fracture, 30 µ m | 550 | % | ISO 527-3 |
| TD, fracture, 30 µ m | 850 | % | ISO 527-3 |
| Drop hammer impact | |||
| 30 µm | 120 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：30 µm | 30 | N | ISO 6383-2 |
| TD：30 µm | 160 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ISO 974 |
| Vicat Softening Temp | 102 | ℃ | ISO 306 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |