| QAMAR FC21HS is a Linear Low Density Polyethylene material. It is available in Africa & Middle East, Asia Pacific, Europe, or North America for blown film. Important attributes of QAMAR FC21HS are: Antiblock Clarity Slip Typical application of QAMAR FC21HS: Film&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Clarity,Smoothness,High anti-blocking |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Tensile modulus | ISO IR 1184 | ||
| MD，30 µm | 190 | MPa | ISO IR 1184 |
| TD，30 µm | 220 | MPa | ISO IR 1184 |
| tensile strength | JIS Z1702 | ||
| MD, fracture, 30 µ m | 55.0 | MPa | JIS Z1702 |
| TD, fracture, 30 µ m | 40.0 | MPa | JIS Z1702 |
| Tensile strain | JIS Z1702 | ||
| fracture | 900 | % | JIS K6760 |
| MD, fracture, 30 µ m | 550 | % | JIS Z1702 |
| TD, fracture, 30 µ m | 850 | % | JIS Z1702 |
| Drop hammer impact | |||
| 30 µm | 120 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：30 µm | 30 | g | ASTM D1922 |
| TD：30 µm | 160 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 |
| Melting temperature | 122 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µm | 9.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 55 | ASTM D2240 | |
| tensile strength | JIS K6760 | ||
| yield | 12.0 | MPa | JIS K6760 |
| fracture | 32.0 | MPa | JIS K6760 |
| Bending modulus | |||
| 23℃ | 260 | MPa | ASTM D747 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 210 | °C | |
| Melt temperature (target) | 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |