Qenos PE MD0592

About
MD0592 is a non-pigmented, high molecular weight MDPE copolymer, developed as a general purpose resin for use in pipe applications. MD0592 contains antioxidants to protect it during extrusion and end use. MD0592 has been designed for extrusion into a full range of non-standard pipe products. MD0592 has been designed to be used as a base resin for striping and jacket compounds for use in pressure pipes made of MD0898. Addition of a UV stabilizer should be considered where the intended application involves intermittent to extended exposure to sunlight. Suitability for use in any application should be determined by appropriate performance testing.&&

About

MD0592 is a non-pigmented, high molecular weight MDPE copolymer, developed as a general purpose resin for use in pipe applications. MD0592 contains antioxidants to protect it during extrusion and end use. MD0592 has been designed for extrusion into a full range of non-standard pipe products. MD0592 has been designed to be used as a base resin for striping and jacket compounds for use in pressure pipes made of MD0898. Addition of a UV stabilizer should be considered where the intended application involves intermittent to extended exposure to sunlight. Suitability for use in any application should be determined by appropriate performance testing.&&

Product Description
Supplier	Qenos
Generic	MDPE
Material Status	Commercial: Active
Features	Weather resistance is good,Inoxidizability,High molecular weight,Copolymer
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.942	g/cm³	ASTM D1505
Melt Flow Rate			ASTM D1238
190℃，21.6kg	13	g/10min	ASTM D1238
190℃，5.0kg	0.60	g/10min	ASTM D1238

THERMAL	Nominal value	Unit	Test method
Oxygen sensing time
210℃	> 20	min	ISO 11357-6

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	62		ASTM D2240
Tensile modulus
1.90 mm	970	MPa	ASTM D638
tensile strength			ASTM D638
Yield, 1.90 mm	21.0	MPa	ASTM D638
Fracture, 1.90 mm	35.0	MPa	ASTM D638
Tensile strain
Fracture, 1.90 mm	900	%	ASTM D638
Bending modulus
1% secant	800	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.