| Quadrant EPP CESTILITE ASTL是一种超高分子量聚乙烯产品,。 它,在欧洲有供货。 典型应用领域为:户外应用。 特性包括: 阻燃/额定火焰 抗静电 良好的抗紫外线能力 良好的韧性 耐磨&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good wear resistance,Antistatic property,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃, 1.00 mm | 0.050 | % | ISO 62 |
| molecular weight | 7000000 | g/mol | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| — | > 90 | kJ/m² | Internal Method |
| Local fracture | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 42.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | |||
| — | 80.0 | ℃ | |
| — | 120 | ℃ | |
| Vicat Softening Temp | 83.0 | ℃ | ISO 306/B |
| Melting temperature | 130 to 135 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~100℃ | 2.0E-4 | 1/℃ | |
| Thermal conductivity coefficient | |||
| 23℃ | 0.40 | W/m/K | |
| Operating temperature | |||
| minimum | -150 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+6 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+6 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Extreme oxygen index | < 20 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative Weight Loss | Internal Method | ||
| — | 85.0 | Internal Method | |
| — | 80.0 | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore D, 3 seconds | 63 | ISO 868 | |
| Shore D, 15 seconds | 61 | ISO 868 | |
| Ball hardness | 37.0 | MPa | ISO 2039-1 |
| Tensile modulus | 770 | MPa | ISO 527-2/1B/1 |
| tensile strength | |||
| yield | 20.0 | MPa | ISO 527-2/1B/50 |
| Tensile strain | |||
| yield | 15 | % | ISO 527-2/1B/50 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2/1B/50 |
| compressive strength | ISO 604/1 | ||
| 1% strain | 5.00 | MPa | ISO 604/1 |
| 2% strain | 9.00 | MPa | ISO 604/1 |
| 5% strain | 15.0 | MPa | ISO 604/1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |