| About |
|---|
| Broadest size range availability Good mechanical and electrical properties Ideal balance of strength and toughness Cast as finished parts and near net shapes (nylon 6)&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Fatigue resistance,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| 24h，23℃ | 0.72 | % | ISO 62 |
| 23℃ | 6.6 | % | ISO 62 |
| Wear rate | 12 | µm/km | ISO 7148-2 |
| Limiting PV at 0.1 / 1 m/s cylindrical sleeve bearings | |||
| 0.13 | MPa.m/s | ||
| 0.08 | MPa.m/s | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 84 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield yld | 5 | % | ISO 527 |
| Broken BRK | 35 | % | ISO 527 |
| Tensile Modulus | 3300 | MPa | ISO 527 |
| Compressive Strength | |||
| 1% | 32 | MPa | ISO 604 |
| 2% | 61 | MPa | ISO 604 |
| 5% | 90 | MPa | ISO 604 |
| Flexural Strength | 131 | MPa | ISO 178 |
| Flexural Modulus | 3580 | MPa | ISO 178 |
| Rockwell hardness | 85 | ISO 2039-2 | |
| Shore hardness | 80 | ISO 868 | |
| Frictional coefficient | 0.4-0.6 | ISO 7148-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 215 | ℃ | ISO 11357-3 |
| Thermal conductivity | 0.29 | W/m/K | |
| Coeff. of linear thermal expansion | |||
| 23℃-60℃ | 80 | µm/(m.K) | |
| 23℃-100℃ | 90 | µm/(m.K) | |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 80 | ℃ | ISO 75-1/-2 |
| Continuous use temperature | 90 | ℃ | |
| Min. service temperature | -30 | ℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Electric strength | 25 | kV/mm | IEC 60243-1 |
| Volume Resistance | 1E14 | ohm·cm | IEC 62631-3-1 |
| Surface Resistivity | 1E13 | ohm | |
| Dielectric Constant | 3.2 | IEC 62631-2-1 | |
| Dissipation Factor | 0.016 | IEC 62631-2-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 3 mm | HB | ||
| Oxygen Index | 25 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 3. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |