| About |
|---|
| Queo 0201FX is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 0201FX is intended for use as primary blend partner in high performance seal layers with an additive package designed to offer improved control of the coefficient of friction of coextruded blown films. Demonstrated applications include: High speed FFS films High strength flexible films Seal layers in food barrier films Laminated structures requiring very high seal integrity Additives Queo 0201FX contains anti block agent, slip agent, processing aid and stabilizers Special Features Queo 0201FX is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. Outstanding toughness Outstanding puncture resistance Unrivalled sealing and hot tack properties at low temperature Low temperature impact strength High clarity Low Coefficient of Friction (C.O.F.) and improved C.O.F. consistency&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | 乙烯基辛烯塑料 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good flexibility |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 1.1 | g/10min | ASTM D1238 | |
| Anti viscosity content | 3000 | ppm | |
| Slippery agent content | 1200 | ppm | |
| thickness | 31.8 | microns | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, yield, 23 ℃, thin film | 4.34 | MPa | ASTM D882 |
| TD, yield, 23 ℃, thin film | 4.96 | MPa | ASTM D882 |
| tensile strength | |||
| MD, fracture, 23 ℃, thin film | 60.5 | MPa | ASTM D882 |
| TD, fracture, 23 ℃, thin film | 63.8 | MPa | ASTM D882 |
| 1% secant modulus (transverse, 23 ℃) | 68.3 | MPa | ASTM D882 |
| 1% secant modulus (longitudinal, 23 ℃) | 74.5 | MPa | ASTM D882 |
| Puncture energy | 2.5 | J | ExxonMobil Method |
| Drop hammer impact | >2274.6 | kn.m | ASTM D1709-A |
| Elongation at break of thin film | |||
| Vertical, 23 ℃ | 720 | % | ASTM D882 |
| Horizontal, 23 ℃ | 470 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 78 | ASTM D2457 | |
| Haze | |||
| μm | 4.4 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 82.8 | ℃ | ASTM D1525 |
| Melting temperature | 95 | ℃ | Internal Method |
| Crystallization temperature | 79 | ℃ | ExxonMobil Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film, Monsanto Dart |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |