| About |
|---|
| Queo 0203 is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 0203 Demonstrated applications include: Seal layers in lamination and flexible barrier films High clarity household articles Specialty cast stretch applications Halogen free flame retardant compounds Lap sealing to OPP Soft foams, e.g. artificial wine corks PP film toughness modification Additives Queo 0203 contains processing stabilizers Special Features Queo 0203 is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. Outstanding toughness Outstanding puncture resistance Unrivalled sealing and hot tack properties at low temperature Low temperature impact strength High clarity Flexibility&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | 乙烯基辛烯塑料 |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | > 1000 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 43 | ISO 868 | |
| tensile strength | |||
| fracture | 31.0 | MPa | ISO 527-2/5A |
| Tensile strain | |||
| fracture | 820 | % | ISO 527-2/5A |
| Bending modulus | 72.0 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| MD | 65.0 | MPa | ASTM D882 |
| Drop hammer impact | |||
| Blown film | > 32 | g | ASTM D1709 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 80.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 96.0 | ℃ | ISO 11357 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 82 | ASTM D2457 | |
| Haze | 2.0 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | 26.5 | J/cm | Internal Method |
| Sealing Initial Temperature | 80 | ℃ | ASTM F88 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film, Monsanto Dart |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |