| About |
|---|
| Queo 0230 is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 0230 Demonstrated applications include: Carpet backing Highly filled compounds Powder coating Extrusion coating Colour master batches Additives Queo 0230 contains a low amount of processing stabilizers Special Features Queo 0230 is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High flexibility and surface softness High clarity Outstanding toughness Excellent low-temperature flex-cracking resistance Outstanding puncture resistance High filler and oil acceptance Low temperature impact strength&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | 乙烯基辛烯塑料 |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,low-temperature impact resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 30 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | < 120 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 38 | ISO 868 | |
| tensile strength | |||
| fracture | 11.0 | MPa | ISO 527-2/5A |
| Tensile strain | |||
| fracture | 880 | % | ISO 527-2/5A |
| Bending modulus | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 71.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 97.0 | ℃ | ISO 11357 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Draw Down | 520 | m/min | |
| Neck-in – 100 m/min | 64.0 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 100 m/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |