Queo™ 7007LA

About
Queo 7007LA – is an ethylene based octene-1 elastomer, produced in a solution polymerisation process using a metallocene catalyst. Applications Queo 7007LA Demonstrated applications include: Seal layers in lamination and flexible barrier films Extrusion coating Surface protection film Cling film Noise reduction in e.g. automotive applications Halogen free flame retardant compounds TPO compounds High strength flexible films Additives Queo 7007LA contains a low amount of processing stabilizers Special Features Queo 7007LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High clarity Low peak melting point Bridging of plastic and elastomeric properties&&

About

Queo 7007LA – is an ethylene based octene-1 elastomer, produced in a solution polymerisation process using a metallocene catalyst. Applications Queo 7007LA Demonstrated applications include: Seal layers in lamination and flexible barrier films Extrusion coating Surface protection film Cling film Noise reduction in e.g. automotive applications Halogen free flame retardant compounds TPO compounds High strength flexible films Additives Queo 7007LA contains a low amount of processing stabilizers Special Features Queo 7007LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High clarity Low peak melting point Bridging of plastic and elastomeric properties&&

Product Description
Supplier	Borealis AG
Generic	乙烯基辛烯塑料
Material Status	Commercial: Active
Features	Good Rigidity,Good Clarity,Halogen free,Flame Characteristics,Octene copolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.870	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	6.6	g/10min
230℃，2.16kg	15	g/10min
Mooney viscosity
ML 1+4，100℃	11	MU	DIN 53523

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, injection molding	无断裂		ISO 180

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -90.0	℃	ISO 974
Vicat Softening Temp	35.0	℃	ISO 306/A
Melting temperature	48.0	℃	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	71
Shaw’s D	< 20
tensile strength
fracture	6.00	MPa	ISO 527-2
Tensile strain
Fracture, injection molding	> 400	%	ISO 527-2
Bending modulus
injection molding	8.00	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.