| About |
|---|
| RABALON® QE546AT is a Thermoplastic Elastomer (TPE) material. It is available in Asia Pacific, Europe, or North America for extrusion. Typical application of RABALON® QE546AT: Automotive&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | TPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 73 | ISO 7619 | |
| tensile strength | |||
| fracture | 13.0 | MPa | ISO 37 |
| 100% strain | 2.7 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 800 | % | ISO 37 |
| Compression deformation | |||
| 70℃，22 hr | 42 | % | ISO 815 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Drying temperature | 60-90 | °C | |
| Drying time | 2.0-6.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| First zone temperature | 120-180 | °C | |
| Zone 2 temperature | 130-190 | °C | |
| Third zone temperature | 140-200 | °C | |
| Fourth zone temperature | 150-210 | °C | |
| Fifth zone temperature | 160-220 | °C | |
| Die temperature | 170-230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 6 sheets, each thickness=2mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |