| About |
|---|
| Radel® R-5600 is a very high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptional hydrolytic stability and toughness superior to other commercially-available, high-temperature engineering resins. They also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Additonal Radel® grades include a transparent injection molding grade (R-5000), an opaque, general purpose, injection molding grade (R-5100) and a transparent, extrusion grade (R-5500). Natural/Transparent: Radel® R-5600 NT Additional Made-to-Order Colors Available&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPSU |
| Material Status | Commercial: Active |
| Features | Alkali resistant,Steam sterilized,Hydrolysis stability,Flame Characteristics,Acidproof,High Heat Resistance,Ultra high toughness,Solvent resistance,Heat Stabilized,High ESCR,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 365℃，5.0kg | 34 to 40 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.37 | % | ASTM D570 |
| balance | 1.1 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.18 mm | 2340 | MPa | ASTM D638 |
| tensile strength | |||
| 3.18 mm | 70.3 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.18 mm | 7.2 | % | ASTM D638 |
| Fracture, 3.18 mm | 60 to 120 | % | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 2340 | MPa | ASTM D790 |
| bending strength | |||
| 5% strain, 3.18 mm | 91.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 690 | J/m | ASTM D256 |
| Tensile impact strength | |||
| 3.18 mm | 399 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 207 | ℃ | ASTM D648 |
| Glass transition temperature | 220 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD：3.2 mm | 5.6E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 3.18 mm | 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 0.0254 mm | > 200 | kV/mm | ASTM D149 |
| 3.18 mm | 15 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 3.18 mm，60 Hz | 3.44 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.76 mm | V-0 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.672 | ASTM D542 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Steam disinfection | |||
| Containing morpholine | > 1000 | Cycles |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 2.5 | hr | |
| Processing (melt) temperature | 360 to 391 | °C | |
| Mold temperature | 138 to 163 | °C | |
| Screw compression ratio | 2.2:1.0 | ||
| Drying temperature | 171 | °C | |
| Drying time | 4.0 | hr | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Heating rate of 36°F (20°C) per minute. |
| 3. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 4. Cycles passed without cracking, crazing, or rupture. Steam Autoclave Conditions: – Temperature: 270°F (132°C) – Time: 30 minutes/cycle – Steam Pressure: 27 psig (0.19 MPa) – Stress Level: 1000 psi (7.0 MPa) in flexure – Additive: Morpholine at 50 ppm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |