| PA66 high viscosity extrusion grade. Natural colour. Suitable for extrusion of tubes, profiles, bars, rods and sheets. Also suitable for injection moulding of high thickness items. ISO 1043 : PA66&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High Viscosity,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 8.4 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 2.1 | % | ISO 62 |
| Viscosity (H2SO4 (sulfuric acid)) | 260 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3250 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 85.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 4.5 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 50 | % | ISO 527-2/1A/50 |
| Bending modulus | 2900 | MPa | ISO 178 |
| bending strength | 110 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 195 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| B50 | 240 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 | |
| Burning rate | 0.0 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | < -20 | °C | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Injection speed | Moderate | ||
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Melt temperature | 270 to 290 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |