| About |
|---|
| PA66 30% glass beads filled injection moulding grade. Natural colour. Suitable for parts requiring low warpage and good surface aspect.&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 1.1 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 7.6 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.7 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | |
| tensile strength | |||
| fracture | 75.0 | MPa | |
| Tensile strain | |||
| fracture | 14 | % | |
| Bending modulus | 3800 | MPa | |
| bending strength | 125 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 3.2 | kJ/m² | |
| 23℃ | 3.7 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 23 | kJ/m² | |
| 23℃ | 28 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 200 | ℃ | |
| 1.8 MPa, unannealed | 65.0 | ℃ | |
| Vicat Softening Temp | 225 | ℃ | |
| Melting temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | ||
| Burning rate | |||
| 3.0 mm | 0.0 | mm/min | |
| Glowing wire flammability index | |||
| 2.0 mm | 700 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | -20 | °C | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 290°C Melt Temperature, 80°C Mold Temperature, 60 MPa Cavity Pressure |
| 3. 0.079 in/min |
| 4. 10°C/min |
| 5. 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |