| PA6/66 copolymer, high viscosity extrusion grade. Natural colour. Suitable for extrusion of cast, blown and co-extruded films, and monofilaments.&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 10 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 3.0 | % | |
| Viscosity (H2SO4 (sulfuric acid)) | 225 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | |
| tensile strength | |||
| yield | 55.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| Nominal tensile fracture strain | > 50 | % | |
| Bending modulus | 1750 | MPa | |
| bending strength | 65.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.2 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | |
| Vicat Softening Temp | 70.0 | ℃ | |
| Melting temperature | 195 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | |
| Flame retardant level | < 10 | mm/min | |
| 0.80 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | -20 | °C | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Injection speed | 中等 | ||
| Melt temperature | 240 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 4. 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |