| PA610 flexible, high viscosity extrusion grade. Toughened and plasticized. Heat stabilized. Natural colour. Suitable for extrusion of pipes, profiles and cable jackets. Good impact resistance also at low temperatures. This grade is partially renewably-sourced (60% of base polymer by weight). |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Viscosity,Renewable resources,low-temperature impact resistance,Plasticizing,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 2.0 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 0.90 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 550 | MPa | |
| tensile strength | |||
| fracture | 36.0 | MPa | |
| 100% strain | 30.0 | MPa | |
| Nominal tensile fracture strain | > 100 | % | |
| Bending modulus | 520 | MPa | |
| bending strength | 18.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 95 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | |
| 1.8 MPa, unannealed | 50.0 | ℃ | |
| Melting temperature | 215 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | -20 | °C | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Injection speed | 中等 | ||
| Melt temperature | 230 to 250 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |