| About |
|---|
| PA610, 30% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour. Suitable for parts requiring good dimensional stability, high stiffness and mechanical resistance. Typical application: automotive fuel system components. This grade is partially renewably-sourced (60% of base polymer by weight).&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Renewable resources,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 2.2 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 145 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.8 | % | ISO 527-2/1A/5 |
| Bending modulus | 7500 | MPa | ISO 178 |
| bending strength | 220 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/Af |
| Melting temperature | 217 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | -20 | °C | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |