| About |
|---|
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Features | high-rigidity |
| Availabilitys | North America,Europe,Asia Pacific,Latin America,Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1500 | kg/m³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 1mm/min | 14400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| 5 mm/min, break | 214 | MPa | ISO 527-2 |
| Tensile Strain | |||
| 5mm/min, break | 3 | % | ISO 527-2 |
| Flexural Modulus | |||
| 2 mm/min | 12800 | MPa | ISO 178 |
| Flexural Strength | |||
| 2 mm/min | 332 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 104 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 10 ℃/min | 220 | ℃ | ISO 11357-1-3 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 210 | ℃ | ISO 75/2 A f |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Melt Temperature | 250-290 | ℃ | |
| Mold Temperature | 80-90 | ℃ | |
| Injection Speed | 中高速 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |