| PA6/Polyolefine Alloy, reduction of water absorption, Impact modified, for injection moulding applications.&& |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PA66 Alloy |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 to 1.05 | g/cm³ | ASTM D792 |
| Density | 1.03 to 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 235℃，5.0kg | 10 | g/10min | ASTM D1238 |
| 235℃，10.0kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | 1.3 | % | ISO 2577 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 3.3 | % | ISO 62 |
| saturated | 3.3 | % | ASTM D570 |
| balance | 1.3 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ASTM D638 |
| Tensile modulus | 1800 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 50.0 | MPa | ASTM D638 |
| yield | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 180 | % | ASTM D638 |
| fracture | 180 | % | ISO 527-2 |
| Bending modulus | 2000 | MPa | ASTM D790 |
| Bending modulus | 2000 | MPa | ISO 178 |
| bending strength | 70.0 | MPa | ASTM D790 |
| bending strength | 70.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 30 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 50 | kJ/m² | ISO 180 |
| 23℃ | 670 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 130 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 130 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |