| About |
|---|
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，3.8kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.10 to 0.30 | % | |
| TD：2.0 mm | 0.20 to 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6600 | MPa | ISO 527-2/1A |
| Tensile stress | 100 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2/1A |
| Bending modulus | 6400 | MPa | ISO 178 |
| Bending stress | 164 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| — | 11 | kJ/m² | |
| -30℃ | 8.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 123 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 240 to 260 | °C | |
| Temperature in the middle of the barrel | 260 to 280 | °C | |
| Front temperature of material barrel | 280 to 300 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |