| About |
|---|
| RAMLLOY PVB702BK23 is Black , Impact Modified,UV Stabilized,Improved Surface Appearance POLYAMIDE 6/ABS, Injection Molding,Automotive Applications |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PA 6+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 23 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.85 to 1.1 | % | |
| TD：2.0 mm | 0.70 to 1.0 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.2 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ISO 527-2/1A |
| Tensile stress | 40.0 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| yield | 3.3 | % | ISO 527-2/1A |
| Bending modulus | 1600 | MPa | ISO 178 |
| Bending stress | 56.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| — | 60 | kJ/m² | |
| -30℃ | 18 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 62.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 192 | ℃ | ASTM D1525 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability | < 100 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 230 to 260 | °C | |
| Temperature in the middle of the barrel | 240 to 260 | °C | |
| Front temperature of material barrel | 240 to 260 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |