| About |
|---|
| RANPELEN SFI-553 is a controlled medium modified polypropylene random copolymer designed for water quenched film technology. It offers an excellent clarity and gloss, a very low haze, a wide hot tack range and a low seal-initiation temperature. It is designed for quality packaging applications, as heat seal layer film. It contains slip and antiblock additives. RANPELEN SFI-553 is suitable for food contact.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Smoothness,High anti-blocking,Food contact compliance,Terpolymer,Low temperature heat sealing |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.0 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 69 | J/m | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| Melting temperature | 135 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µ m, cast thin film | < 2.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Seal Temperature（30.0 µm） | 125 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 77 | ISO 2039-2 | |
| tensile strength | |||
| yield | 22.6 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 500 | % | ISO 527-2 |
| Bending modulus | 735 | MPa | ISO 178 |
| friction coefficient | |||
| Casting thin film | < 1.0 | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cast Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |