| VA-1500 is a 50 shore A polyurethane elastomer formulated for hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. VA-1500 has excellent green strength for quick demold times.&& |
| Product Description | |
|---|---|
| Generic | TSU |
| Material Status | Commercial: Active |
| Features | Good Green Strength |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| Curing treatment | 1.08 | g/cm³ | |
| Hardener | 1.08 | g/cm³ | |
| Matrix resin | 1.18 | g/cm³ | |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | ASTM D2566 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| resin | 按容量计算的混合比: 37 按重量计算的混合比: 40 | ||
| Hardening method | 按容量计算的混合比: 100 按重量计算的混合比: 100 | ||
| stripping time | 30 to 60 | min |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| viscosity | |||
| 25℃ | 0.60 | Pa·s | |
| 25℃ | 0.90 | Pa·s | |
| 25℃ | 1.3 | Pa·s | |
| Curing time | 25 | hr | |
| Gelation time | 4.0 to 6.0 | min |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 45 to 55 | ASTM D2240 | |
| tensile strength | 2.41 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 160 | % | ASTM D638 |
| tear strength | 7.01 | kN/m | ASTM D624 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Hardener |
| 3. Mixed |
| 4. Resin |
| 5. 24 hours at 77°F + 1 hour at 150°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |