| About |
|---|
| Description: Product is based on standard grade saturated polyester and has strong resilience and tear resistance, excellent abrasion resistance, higher resistance to hydrolysis failure and oxidation, good stability towards solvents and light. Application: Wheel, shoes, injection part etc.&& |
| Product Description | |
|---|---|
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Inoxidizability,Elastic,Good tear strength,Good wear resistance,Solvent resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183/A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 43.0 | MPa | ISO 37 |
| 100% strain | 14.0 | MPa | |
| 300% strain | 27.0 | MPa | |
| Tensile strain | |||
| fracture | 520 | % | ISO 37 |
| tear strength | 190 | kN/m | ISO 34-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 95 | ||
| Shaw’s D | 50 | ||
| abrasion resistance | 40.0 | mm³ | ISO 4649 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Barrel rear temperature | 200 | °C | |
| Barrel middle temperature | 210 | °C | |
| Barrel front temperature | 215 | °C | |
| Nozzle temperature | 220 | °C | |
| Injection pressure | 70.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |