| About |
|---|
| Reclair O 21010, is an Octene comonomer based linear low density polyethylene with optimum level of antioxidant and polymer processing aid but without slip additive and antiblocking agent. This grade is designed for lamination film applications where good optical properties and adhesion to the substrate are required.&& |
| Product Description | |
|---|---|
| Supplier | Reliance |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Optical performance,Good bond,Inoxidizability |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.50 | ASTM D1894 | |
| With oneself – static | 0.58 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield, 40 µ m | 12.5 | MPa | ASTM D882 |
| TD, yield, 40 µ m | 13.0 | MPa | ASTM D882 |
| MD, fracture, 40 µ m | 45.0 | MPa | ASTM D882 |
| TD, fracture, 40 µ m | 40.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 40 µ m | 750 | % | ASTM D882 |
| TD, fracture, 40 µ m | 950 | % | ASTM D882 |
| Drop hammer impact | |||
| 40 µm | 280 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：40 µm | 550 | g | ASTM D1922 |
| TD：40 µm | 1100 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 80 | ASTM D523 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |