| About |
|---|
| Repol C080MT is recommended for use in Injection Moulding processes where high impact strength is required. It is an ideal material to use in making battery containers, automotive and industrial products. Repol C080MT contains long term heat stabiliser as required for under-the-hood applications in automotive.&& |
| Product Description | |
|---|---|
| Supplier | Reliance |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, injection molding | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, injection molding | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, injection molding | 1050 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, injection molded | 100 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |