| About |
|---|
| Product Description | |
|---|---|
| Supplier | Dainichiseika |
| Material Status | Commercial: Active |
| Features | Mechanical property,Grease resistance,Heat Resistance, Good,Good wear resistance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| proportion | 1.2±0.03 | JIS Z-8807 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | 90±2 | Shore A | JIS K-7311 |
| Tensile modulus | 6.1±1.2 | MPa | JIS K-7311 |
| tensile strength | ≥34.3 | MPa | JIS K-7311 |
| elongation at break | ≥400 | % | JIS K-7311 |
| tear strength | ≥93.1 | kN/m | JIS K-7311 |
| Compression permanent deformation | 55 | % | JIS K-6301 |
| Taber abraser | 37 | % | JIS K-6301 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | <-70 | ℃ | JIS K-7311 |
| Flow start-up temperature | 190 | ℃ | JIS K-6301 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| extrusion | Nominal value | Unit | Test method |
| Post stage temperature | 170 | ℃ | |
| Mid section temperature | 180 | ℃ | |
| Front temperature | 190 | ℃ | |
| Nozzle temperature | 195 | ℃ | |
| Feed area | 160-170 | ℃ | |
| transition region | 180-190 | ℃ | |
| Measurement area | 190-200 | ℃ | |
| Mold temperature | 190-200 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |