| Resilience™ LS11001E是一种刚硬聚氯乙烯产品,。 它可以通过挤出进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 典型应用领域为:照明设备。 特性包括: 阻燃/额定火焰 耐冲击&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | High impact resistance,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| PVC unit classification | 13364 | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| TD, 23 ℃, 3.2mm, molded | 190 | J/m | ASTM D256-A |
| Flow rate, 23 ℃, 3.18mm, molded | 200 | J/m | ASTM D256-A |
| Falling impact resistance | ASTM D4226 | ||
| 23℃ | 64.9 | J/cm | ASTM D4226 |
| 23℃ | 159 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 70.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.3E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.90 mm, all colors | V-0 | UL 94 | |
| 1.50 mm, all colors | 5VA | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ease of sizing | Good |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 83 | ASTM D2240 | |
| Tensile modulus | 3300 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 44.7 | MPa | ASTM D638 |
| Bending modulus | 3100 | MPa | ASTM D790 |
| bending strength | 83.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 182 to 193 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |