| About |
|---|
| Resirene 2970 is a MIPS grade suitable for injection molding processes.&& |
| Product Description | |
|---|---|
| Generic | PS (MIPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High liquidity,Quick molding cycle,HB |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 12 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2110 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 19.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 47 | % | ASTM D638 |
| Bending modulus | 2070 | MPa | ASTM D790 |
| bending strength | 33.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 3.2mm | 69 | J/m | ASTM D256 |
| 12.7mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 72.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 80.0 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 85 | ASTM D2457 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |