| About |
|---|
| Revolve M-686 is a fully formulated rotomoulding resin especially suitable for large tank applications. Additionally this grade carries WRC approval for potable water applications (Cert No. 0311501) and it is designed to meet the requirements of BS4213. It has a high (2% min) carbon black content for extra UV stability and opacity.&& |
| Product Description | |
|---|---|
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,High impact resistance,Good Hardness |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.939 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 3.5 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 10% non-ionic detergent | 478 | hr | ASTM D1693 |
| 100% non-ionic detergent | > 1000 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 20.5 | MPa | ISO 527-2/50 |
| Bending modulus | 820 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature shock | |||
| ARM，3.00 mm | 95.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |