RheTech Thermoplastic Polyolefin FT7013-720UV

About
Thermoplastic Polyolefin, 230K Flexural Modulus, UV Stabilized, XTM Dark Sandstone&&

Product Description
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Weather resistance is good
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.11	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	12	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	61		ASTM D2240
tensile strength	17.2	MPa	ASTM D638
Bending modulus	1590	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	210	J/m	ASTM D256
Drop hammer impact	18.1	J	ASTM D5420

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	53.3	℃	ASTM D648
0.45 MPa, unannealed	96.7	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	66 to 82	°C
Drying time	1.0 to 2.0	hr
Recommended maximum moisture content	0.050	%
Barrel rear temperature	204 to 232	°C
Barrel middle temperature	210 to 238	°C
Barrel front temperature	216 to 243	°C
Nozzle temperature	221 to 232	°C
Mold temperature	27 to 49	°C
Injection pressure	2.76 to 10.3	MPa
Hold pressure	2.07 to 8.27	MPa
Back pressure	0.345 to 1.03	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.