| About |
|---|
| Polypropylene compound filled with 65% calcium carbonate. Application suggested as a masterbatch in furnishing. Available in the versions natural and colored as per sample.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Homopolymer,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 16 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.75 | % | ISO 294-4 |
| MD | 0.75 | % | ISO 294-4 |
| Ash Content | 65 | % | ISO 3451 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 64.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 102 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 78 | ISO 868 | |
| tensile strength | |||
| Yield, 23 ℃ | 13.0 | MPa | ISO 527-2/20 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.0 | % | ISO 527-2/20 |
| Bending modulus | |||
| 23℃ | 4500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 23.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 210 to 230 | °C | |
| Mold temperature | 50 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |