| About |
|---|
| Riblene FM 34 E is a low density polyethylene (LDPE), additivated with slip (erucamide) and antiblocking agent, suitable for blown film extrusion. Riblene FM 34 E is characterised by a good balance between processability, mechanical and optical properties. Films manufactured by Riblene FM 34 E are easily heat shrinkable. Main Application Riblene FM 34 E is recommended for general blown film applications, for the production of thin trasparent film, for garment and newspaper packaging, freezer bags and blend.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Smoothness,Optical performance,High anti-blocking,Food contact compliance,Low density,Good thermal contraction |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | 0.11 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| film thickness | 18 to 50 µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 40 µ m, blow molded film | 190 | MPa | |
| 1% secant, TD, 40 µ m, blow molded film | 200 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 40 µ m, blow molded film | 11.0 | MPa | |
| MD, fracture, 40 µ m, blow molded film | 21.0 | MPa | |
| TD, fracture, 40 µ m, blow molded film | 20.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 300 | % | |
| TD, fracture, 40 µ m, blow molded film | 600 | % | |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 110 | g | ISO 7765-1 |
| tear strength | ISO 6383-2 | ||
| MD，40 µm | 80.0 | kN/m | |
| TD，40 µm | 55.0 | kN/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 93.0 | ℃ | ISO 306/A |
| Melting temperature | 113 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 72 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 6.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 170 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |