| Rigidex HD5211EA-Y is a high density polyethylene copolymer grade with a narrow molecular weight distribution, suitable for spinning and multifilaments.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good liquidity,Low speed solidification point,Weight distribution,Copolymer,High density,Solvent resistance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ISO 1872 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 11 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ISO 868 | |
| tensile strength | |||
| Yield, 23 ℃ | 26.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1000 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 123 | ℃ | ISO 306/A |
| Melting temperature | 131 | ℃ | ASTM D2117 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-4 | 1/℃ | ASTM D696 |
| specific heat | 2300 | J/kg/℃ | |
| Thermal conductivity coefficient | 0.48 | W/m/K | ASTM C177 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2nd Heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |