| About |
|---|
| Rigidex® HD6007S is a medium molecular weight polyethylene grade supplied in pellet form for use in a wide range of blow moulding and extrusion applications. Typical applications Lightweight containers produced at high speeds, e.g. bottles for packaging powders, milk and chemical products which have a low environmental stress cracking activity Benefits and Features Very easy processing High rigidity Good surface finish&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High density,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.962 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.60 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃，BTT，F50 | 20.0 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 30.5 | MPa | ISO 527-2/2/100 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 300 | % | ISO 527-2/2/100 |
| Bending modulus | |||
| 23℃ | 1700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Bottle Stress Crack Resistance（60℃） | 1.0 | hr | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 3.9 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |