| About |
|---|
| Rilsamid® AECV BLACK T8L resin is a black colored polyamide 12. This grade is designed for cable coating.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，2.16 kg | 12.0 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.6 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1350 | MPa | |
| tensile strength | |||
| yield | 41.0 | MPa | |
| Tensile strain | |||
| yield | 5.0 | % | |
| Nominal tensile fracture strain | > 50 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | — | kJ/m² | |
| 23℃ | — | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | — | ||
| 23℃ | — | ||
| Multi axial instrumented impact energy | |||
| -30℃ | — | J | |
| Multi axial instrumented peak impact force | |||
| -30℃ | — | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 135 | ℃ | |
| 1.8 MPa, unannealed | 55.0 | ℃ | |
| Vicat Softening Temp | 138 | ℃ | |
| Melting temperature | 178 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | — | ohms·cm | |
| Dielectric strength | — | kV/mm | |
| Relative permittivity | |||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation factor | |||
| 100 Hz | 0.043 | ||
| 1 MHz | 0.019 | ||
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 3.2 mm | V-2 | ||
| 1.6 mm | HB | ||
| Extreme oxygen index | 22 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |