| About |
|---|
| Rilsamid® AESN BLACK P302 TL resin is a black colored polyamide 12. This grade is plasticized and designed for tube extrusion. Rilsamid® AESN BLACK P302 TL resin falls into the PA12-HIPHL category according to DIN 73378.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 235℃，5 kg | 18.0 | cm³/10min | ISO 11357 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 71 | ISO 868 | |
| Shore D, 15 seconds | 64 | ISO 868 | |
| Tensile modulus | 400 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 54.0 | MPa | ISO 527-2 |
| yield | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 200 | % | ISO 527-2 |
| yield | 26 | % | ISO 527-2 |
| Bending modulus | 350 to 450 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 6.00 | mg | ISO 9352 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 6.0 | kJ/m² | ISO 179 |
| 23℃ | No Break | ISO 179 | |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 173 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA12-HIP, EHL, 22-004 | ISO 1874 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Melt temperature | 200 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |