| Rilsamid® AESNO P10 TL resin is a plasticized conductive grade designed for tube extrusion. AESNO P10 TL resin is a natural polyamide 12. This grade is plasticized and designed for tube extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Plasticizing,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| saturated | 0.70 | % | ASTM D570 |
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 32 | J/m | ASTM D256 |
| 23℃ | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 48.9 | ℃ | ASTM D648 |
| Melting temperature | 174 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 68.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 330 | % | ASTM D638 |
| Bending modulus | 758 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 94 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |