| About |
|---|
| Rilsan ® Clear G 170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications. MAIN APPLICATIONS Coffee machine. Fuel filter container. Inner layer of fiber optic and copper telephone cables resistant to rodents. Power cables resistant to rodents.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA 11 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD：40℃，2.0 mm，24 hrs | 0.72 | % | Internal Method |
| MD：40℃，2.0 mm，24 hrs | 0.69 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | ISO 62 |
| 23℃，24hr | 3.8 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 84 | ISO 868 | |
| Shore D, 15 seconds | 79 | ISO 868 | |
| Tensile modulus | 2020 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 58.0 | MPa | ISO 527-2 |
| yield | 74.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 100 | % | ISO 527-2 |
| yield | 9.0 | % | ISO 527-2 |
| Bending modulus | 1980 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 13 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 136 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| Glass transition temperature | 168 | ℃ | ISO 11357-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2000 µm，560 nm | 90.8 | % | ASTM D1003 |
| Refractive index | 1.5380 | ISO 489 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 270 to 310 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Melt temperature | 270 to 290 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |