| About |
|---|
| Rilsan® HT CESV BLACK P010 TL resin is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high-temperature automotive and other demanding technical applications.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，2.16 kg | 0.500 | cm³/10min | ISO 1133 |
| 300℃，5 kg | 3.10 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 14 | kJ/m² | ISO 179 |
| 23℃ | 76 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 无断裂 | ISO 179 | |
| 23℃ | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Hoop Stress | |||
| 23℃ | 30.0 | MPa | |
| 150℃ | 5.00 | MPa | |
| Renewable Carbon Conent | > 45 | % | ASTM D6866 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 74 | ISO 868 | |
| Shore D, 15 seconds | 64 | ISO 868 | |
| Tensile modulus | 880 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 41.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 130 | % | ISO 527-2 |
| Bending modulus | 820 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Melt temperature | 270 to 300 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |