| About |
|---|
| Rilsan® TMNO TLD resin is a stabilized Polyamide 1010 resin neat produced from a renewable source. This grade is designed for injection molding applications.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA 1010 |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1400 | MPa | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 7.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| Melting temperature | 202 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Renewable Carbon Conent | > 98 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 220 to 280 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |