| About |
|---|
| Rilsan® TZM 30 BLACK TL is a stabilized Polyamide 1010 resin reinforced with 30% glass fiber. This black grade is designed for injection molding application.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA 1010 |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.70 | % | |
| MD | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7400 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 136 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 11 | kJ/m² | |
| 23℃ | 19 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 95 | kJ/m² | |
| 23℃ | 95 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 195 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 185 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 190 | ℃ | ISO 306 |
| Melting temperature | 202 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Renewable Carbon Conent | > 95 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 240 to 290 | °C | |
| Mold temperature | 60 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |