| Romiloy® 5720 UV是一种聚碳酸酯+聚丁烯对苯二甲酸酯（PC+PBT）材料,。 该产品在欧洲有供货,加工方式为:注射成型。 Romiloy® 5720 UV的主要特性有: 阻燃/额定火焰 紫外线稳定 耐化学品 良好的抗紫外线能力&& |
| Product Description | |
|---|---|
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Solvent resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 38 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 23℃ | 0.40 to 0.60 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2380 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2350 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 92.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 40 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 89.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 117 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | < 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Proposed maximum recycled material ratio | 5 | % | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 230 to 260 | °C | |
| Processing (melt) temperature | < 260 | °C | |
| Mold temperature | 60.0 to 90.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |